The paper presents the technology for obtaining NiFe/Ti/NiFe layer structures in MEMS technology using magnetron purge with the assumption of being used as semi-magnetic sensors. A series of samples was made on a glass substrate with a sandwich structure, where the individual layers were 100 nm NiFe, 10 nm Ti and on top again NiFe with a thickness of 100 nm. Measurements of DC resistance of the obtained structures in a constant magnetic field, which was produced by neodymium magnets and an electromagnet, were carried out. The obtained results confirm the occurrence of phenomena known as the magnetoresistance effect. The influence of the spatial arrangement of structures relative to the constant magnetic field vector was checked and proved.

W pracy przedstawiono technologię otrzymywania struktur warstwowych NiFe/Ti/NiFe w technologii MEMS metodą ro z pylania magnetronowego w założeniu mających służyć jako czujniki pół magnetycznych. Wykonano serię próbek na szklanym podłożu o budow ie kana pkowej, gdzie poszczególne warstwy stanowiły 100 nm NiFe,10 nm Ti oraz na wierzchu ponownie NiFe o grubości 100 nm. Przeprowadzono pomiary rezystancji stałoprądowej otrzymanych struktur w stałym polu magnetycznym, które było wytwarzane przez magnesy neodym owe oraz elektromagnes. Otrzymane wyniki potwierdzają występowanie zjawisk określanych jako efekt magnetooporowy. Sprawdzony oraz udowodniony został wpływ ułoż enia przestrzennego struktur względem wektora stałego pola magnetycznego.